Effect of Isothermal Hold on the Microstructural Evolution of the Stainless Steel 304L/Zircaloy-4 Interface

The transition from solid-state bonding of the stainless steel 304L/Zircaloy-4 diffusion couple to a partial liquid-phase bonding is important for the bonding process at temperatures ranging from 950 to 1050 °C. In this study, the temperature at which a melting process occurs at the interface after 45 min of isothermal holdings is determined experimentally. This melting process leads to a drastic change in the thickness of the reaction products zone (RPZ) as well as on its microstructure. Diffusion couples were characterized by SEM-EDS, and quantitative chemical analyses of different phases are performed by EPMA. The RPZ consists of three layers: the (α-Fe-Cr) phase layer and two layers consisting of Zr(Fe,Cr)2 (e), Zr2(Fe,Ni) and (α-Zr) phases. The thickness of these layers strongly depends on the holding temperature. The analysis allowed the description of the physicochemical phenomena occurring during isothermal holding as well as during cooling. The solidification paths are determined at 1000, 1020 and 1050 °C. Hardness tests are performed on the bonded samples in order to qualify the mechanical properties of different phases of the RPZ. This study leads to a better understanding of the complex phenomena intervening in the joining process which is very useful for applications in industrial scale.