HfO2-based InP n-channel metal-oxide-semiconductor field-effect transistors and metal-oxide-semiconductor capacitors using a germanium interfacial passivation layer

In this letter, we present our experimental results of HfO2-based n-channel metal-oxide-semiconductor field-effect transistors (MOSFETs) and metal-oxide-semiconductor capacitors (MOSCAPs) on indium phosphide(InP) substrates using a thin germanium (Ge) interfacial passivation layer (IPL). We found that MOSCAPs on n-InP substrates showed good C-V characteristics such as a small capacitance equivalent thickness (14A), a small frequency dispersion (<10% and <200mV), and a low dielectric leakage current (∼5×10−4A∕cm2 at Vg=1.5V), whereas MOSCAPs on p-InP exhibited poor characteristics, implying severe Fermi level pinning. It was also found that InP was more vulnerable to a high temperature process such that C- V curvesshowed a characteristic “bump” and inversion capacitance at relatively high frequencies. From n-channel MOSFETs on a semi-insulating InP substrate using Ge IPL, HfO2, and TaN gate electrodes, excellent electrical characteristics such as a large transconductance (9.3mS∕mm) and large drain current...