Efficiency of solution-processed multilayer polymer light-emitting diodes using charge blocking layers

By blending semiconducting polymers with the cross-linkable matrix ethoxylated-(4)-bisphenol-a-dimethacrylate (SR540), an insoluble layer is acquired after UV-illumination. Following this approach, a trilayer polymer light-emitting diode (PLED) consisting of a blend of poly[N,N′-bis(4-butylphenyl)-N,N′-bis(phenyl)- benzidine] (poly-TPD) and SR540 as an electron-blocking layer, Super Yellow- Poly(p-phenylene vinylene) (SY-PPV) blended with SR540 as an emissive layer, and poly(9,9-di-n-octylfluorenyl-2,7-diyl) as a hole-blocking layer is fabricated from solution. The trilayer PLED shows a 23% increase in efficiency at low voltage as compared to a single layer SY-PPV PLED. However, at higher voltage, the advantage in current efficiency gradually decreases. A combined experimental and modelling study shows that the increased efficiency is not only due to the elimination of exciton quenching at the electrodes but also due to suppressed nonradiative trap-assisted recombination due to carrier confinement. At high ...